JT04 Anti Fog Cross-Linked Shrink Film

                                   

	

		

			
TEST ITEM
			
UNIT
			
ASTM TEST
			
TYPICAL VALUES
		
	
	

		

			
THICKNESS
			
 
			
 
			
12um
			
15um
			
19um
			
25um
		
		

			
TENSILE
		
		

			
Tensile Strength (MD)
			
N/mm2
			
D882
			
121
			
126
			
131
			
131
		
		

			
Tensile Strength (TD)
			
111
			
116
			
121
			
126
		
		

			
Elongation (MD)
			
%
			
121
			
126
			
131
			
136
		
		

			
Elongation (TD)
			
111
			
116
			
121
			
126
		
		

			
TEAR
		
		

			
MD
			
g
			
D1922
			
11.1
			
13.1
			
16.6
			
24.1
		
		

			
TD
			
10.1
			
11.6
			
15.1
			
22.6
		
		

			
SEAL STRENGTH
		
		

			
MD/Hot Wire Seal
			
N/mm
			
F88
			
1.20
			
1.43
			
1.80
			
2.35
		
		

			
TD/Hot Wire Seal
			
1.10
			
1.33
			
1.70
			
2.15
		
		

			
COF(film to Film)
		
		

			
Dynamic
			
 
			
D1894
			
0.41
			
0.39
			
0.37
			
0.36
		
		

			
Static
			
 
			
0.42
			
0.40
			
0.38
			
0.37
		
		

			
OPTICS
		
		

			
Haze
			
 
			
D1003
			
3.9
			
4.9
			
5.6
			
5.9
		
		

			
Clarity
			
 
			
D1746
			
95.6
			
94.6
			
93.6
			
91.1
		
		

			
Gloss @ 45Deg
			
 
			
D2457
			
82.1
			
80.1
			
78.6
			
76.1
		
		

			
Antifog arrival time at 5℃
			
2 Hours
		
		

			
Antifog Effect
			
Complete transparent, no visible water
		
		

			
BARRIER
		
		

			
Oxygen Transmission Rate
			
cc/m2/day
			
D3985
			
9600
			
8700
			
6200
			
4900
		
		

			
Water Vapor Transmission Rate
			
gm/m2/day
			
F1249
			
30.8
			
27.4
			
19.6
			
16.6
		
		

			
SHRINKAGE PROPERTIES
			
MD
			
TD
		
		

			
Free Shrinkage
			
100℃
			
%
			
D2732
			
21
			
31
		
		

			
110℃
			
31
			
46
		
		

			
120℃
			
63
			
65
		
		

			
130℃
			
82
			
79
		
		

			
Shrink Tension
			
100℃
			
Mpa
			
D2838
			
2.25
			
2.60
		
		

			
110℃
			
2.90
			
4.00
		
		

			
120℃
			
3.40
			
4.25
		
		

			
130℃
			
3.41
			
3.95
		
	


Note: This infor mation represents our best judgment on the work done,but the company assumes no liability whatsoever in connection with the use of infomation or findings contained herein.