JT02 Hot Slip Shrink Film

                                   

	

		

			
TEST ITEM
			
UNIT
			
ASTM TEST
			
TYPICAL VALUES
		
	
	

		

			
THICKNESS
			
 
			
 
			
12um
			
15um
			
19um
			
25um
		
		

			
TENSILE
		
		

			
Tensile Strength (MD)
			
N/mm2
			
D882
			
111
			
111
			
106
			
91
		
		

			
Tensile Strength (TD)
			
106
			
106
			
101
			
86
		
		

			
Elongation (MD)
			
%
			
111
			
116
			
121
			
126
		
		

			
Elongation (TD)
			
106
			
111
			
111
			
121
		
		

			
TEAR
		
		

			
MD
			
g
			
D1922
			
11.1
			
14.1
			
16.1
			
24.1
		
		

			
TD
			
9.6
			
12.1
			
15.1
			
22.1
		
		

			
SEAL STRENGTH
		
		

			
MD/Hot Wire Seal
			
N/mm
			
F88
			
0.78
			
0.93
			
1.20
			
1.30
		
		

			
TD/Hot Wire Seal
			
0.81
			
0.95
			
1.18
			
1.43
		
		

			
COF(film to Film)
		
		

			
Dynamic
			
 
			
D1894
			
0.29
			
0.27
			
0.26
			
0.29
		
		

			
Static
			
 
			
0.30
			
0.28
			
0.27
			
0.30
		
		

			
Static (Hot Slip) @ 60℃
			
 
			
0.37
			
0.36
			
0.35
			
0.33
		
		

			
OPTICS
		
		

			
Haze
			
 
			
D1003
			
2.4
			
2.9
			
3.7
			
4.2
		
		

			
Clarity
			
 
			
D1746
			
97.3
			
96.6
			
96.1
			
95.1
		
		

			
Gloss @ 45Deg
			
 
			
D2457
			
86.1
			
84.1
			
83.6
			
82.1
		
		

			
BARRIER
		
		

			
Oxygen Transmission Rate
			
cc/m2/day
			
D3985
			
11800
			
11000
			
8500
			
6700
		
		

			
Water Vapor Transmission Rate
			
gm/m2/day
			
F1249
			
48.6
			
37.6
			
28.7
			
23.6
		
		

			
SHRINKAGE PROPERTIES
			
MD
			
TD
			
MD
			
TD
		
		

			
Free Shrinkage
			
100℃
			
%
			
D2732
			
21
			
30
			
21
			
27
		
		

			
110℃
			
39
			
44
			
36
			
46
		
		

			
120℃
			
59
			
62
			
57
			
61
		
		

			
130℃
			
66
			
67
			
65
			
66
		
		

			
Shrink Tension
			
100℃
			
Mpa
			
D2838
			
1.80
			
2.65
			
1.95
			
2.75
		
		

			
110℃
			
2.70
			
3.50
			
2.80
			
3.55
		
		

			
120℃
			
2.90
			
3.65
			
2.95
			
3.75
		
		

			
130℃
			
2.65
			
3.35
			
2.75
			
3.40
		
	


Note: This infor mation represents our best judgment on the work done,but the company assumes no liability whatsoever in connection with the use of infomation or findings contained herein.